Hydrotite For Joint Repair, Control Joints, Etc. Waterstop

Hydrotite is a state-of-the-art hydrophilic waterstop with unmatched durability and watersealing capacity. Comprised of Non-Bentonite, modified chloroprene rubber, Hydrotite expands up to EIGHT TIMES its original volume when exposed to water. This expansion creates an effective compression sealwithin joints of limited movement. Recognized worldwide, Hydrotite has a proven track record as a high quality and cost effective solution to your water containment needs. Leakmaster LV-1 is a single component water-swelling sealant with excellent and unique properties. Leakmaster may be applied in locations where conventional solid sealants cannot be easily applied.

Hydrotite Waterstop Physical Properties

Property	Test Method	Unit	Hydrophilic	Rubber	Chloroprene	Rubber
			Minimum	Typical	Minimum	Typical
Tensile Strength	ASTM D412	lb/in2	350	366	1300	1570
Elongation	ASTM D412	%	600	670	400	450
Hardness	ASTM D2240	Shore A	52+/-5	54	50+/-5	50
Tear Resistance	ASTM D624	lb/in	50	60.3	100	123
Specific Gravity	ASTM D792		1.32+/-0.1	1.32	1.38+/-0.1	1.38

Leakmaster Physical Properties

General Properties

Appearance	Putty-Like
Color	Grey
Specific Gravity	1.30
Extrudability	Within 20 seconds (at 23¡C)
Slump	3mm max. (at 23¡C)
Tack-Free Time	Within 8 hours (at 23¡C, 60% R.H.)
	JIS-A-5758

Properties AFTER HARDENING

Hardness	35 Shore A
Tensile Strength	Tensile Strength
Elongation	1250%
Tear Strength	10 kgf/cm (56 lb/in)
	JIS-K-6301

Adhesion Properties

Hardness	Steel	Aluminum	Mortar
50% Modulus (kgf/cm2)	4.5 64 psi	6.5 92 psi	6.5 92 psi
Max. Tensile Strength (kgf/cm2)	7.0 99 psi	12.2 173 psi	11.1 157 psi
Elongation at Break (%)	330	580	570